Adsorption of Pb(II) from Water onto ZnO, TiO2, and Al2O3: Process Study, Adsorption Behaviour, and Thermodynamics

This study is aimed at comparing the use of zinc oxide (ZnO), titanium dioxide (TiO2), and aluminium oxide (Al2O3) for removing lead ions from water through adsorption. The point of zero charge was obtained for ZnO, TiO2, and Al2O3 and was found to be 7.3, 7.1, and 9.0, respectively. The effect of pH, adsorbent dose, contact time, initial concentrations, and temperature was investigated in batch experiments. The optimal conditions obtained were 7, 2 g/L, 120 mins, 100 ppm, and 41° C, respectively, where the optimal removal efficiencies were 98.43%, 96.45%, and 85.50% for ZnO, TiO2, and Al2O3, respectively. In addition, analyses of adsorption kinetics, mechanisms, isotherms, and thermodynamics were performed. The adsorption kinetics of Pb(II) were compared to popular models, and it was found that the pseudo-second-order (PSO) model best fitted the Pb(II) uptake for all adsorbents at correlation coefficient (R2 ≥ 0:96). The adsorption isotherms of Pb(II) were also compared to popular models, and it was found that the Pb(II) uptake by TiO2 and ZnO was well-described by the Langmuir model (R2 ≥ 0:96) with maximum adsorption capacities of 55.04 and 58.88 mg/g, respectively. On the other hand, the behaviour of Al2O3 is described more accurately by the Dubinin-Radushkevich (D-R) model (R2 = 0:96), and the maximum adsorption capacity was 53.64 mg/g. The isotherm analysis proved that the limiting step of the adsorption process is the film diffusion mechanism. In addition, studying the heat of adsorption of Pb(II) implied that the adsorption is endothermic due to the positive values of enthalpy (ΔH° ≥ 30) for all adsorbents. The absorbents were characterized using scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX) to study the morphology of surfaces and the chemical characterization of the adsorbents to ensure that adsorption is achieved. ZnO showed better performance for the uptake of lead followed by TiO2 then Al2O3